Caractérisation microstructurale 3D et densification locale d'isolants fibreux cellulosiques sollicités en compression
Résumé
In this work, we focus on a thermal insulating panel made of wood fibres. The making process is a non-woven fabric process that generates a high porosity and a very lowdensity material. Thermal properties were first investigated. This paper deals with mechanical properties that are involved in the production line, transport and handling in the construction site. An insulating panel was compressed (33% and 73%) and we followed insitu its internal deformation using X-ray microtomography. The results enlighten a special behaviour that is linked to the low-density structure of the panel. In particular, the fibres are not compressed and the macroscopic deformation of the sample generates only a new organisation of the fibres in the panel. These results are confirmed by morphological measurements that were performed by 3D image analysis.
On s'intéresse à des isolants thermiques à base de fibres de bois utilisés dans le bâtiment, de très forte porosité, élaborés par un procédé textile non tissé. Les propriétés thermiques ont fait l'objet des premières études et les propriétés mécaniques, intervenant lors du transport et de la manipulation, font l'objet de ce travail. Nous avons suivi in situ, grâce à la microtomographie X, les états de déformation interne d'un panneau d'isolation soumis à une sollicitation de compression transverse (33 % et 73 %). Le comportement particulier mis en lumière par l'accès à la déformation locale est relié à la très faible densité du matériau. En particulier, les fibres de bois ne sont pas individuellement mécaniquement comprimées et la déformation macroscopique du matériau n'engendre que leur réorganisation spatiale. Ces résultats sont mis en relation avec des caractéristiques morphologiques de structures évaluées par analyse d'image 3D.
Origine : Fichiers produits par l'(les) auteur(s)
Loading...